EN-MC21210 magnesium belongs to the magnesium alloys classification, while solder alloy 133 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21210 magnesium and the bottom bar is solder alloy 133.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
33
Elongation at Break, % 14
34
Poisson's Ratio 0.29
0.4
Shear Modulus, GPa 17
12
Tensile Strength: Ultimate (UTS), MPa 190
41

Thermal Properties

Latent Heat of Fusion, J/g 350
42
Melting Completion (Liquidus), °C 600
220
Melting Onset (Solidus), °C 570
180
Specific Heat Capacity, J/kg-K 1000
180
Thermal Conductivity, W/m-K 120
47
Thermal Expansion, µm/m-K 27
25

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24
11
Electrical Conductivity: Equal Weight (Specific), % IACS 130
10

Otherwise Unclassified Properties

Density, g/cm3 1.6
9.3
Embodied Carbon, kg CO2/kg material 24
9.4
Embodied Energy, MJ/kg 160
160
Embodied Water, L/kg 980
840

Common Calculations

Stiffness to Weight: Axial, points 15
2.0
Stiffness to Weight: Bending, points 72
12
Strength to Weight: Axial, points 32
1.2
Strength to Weight: Bending, points 44
2.9
Thermal Diffusivity, mm2/s 76
29
Thermal Shock Resistance, points 11
3.5

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.6 to 2.6
0 to 0.0010
Antimony (Sb), % 0
0.2 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Copper (Cu), % 0 to 0.010
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.0050
0 to 0.020
Lead (Pb), % 0
48.5 to 50.3
Magnesium (Mg), % 96.3 to 98.3
0
Manganese (Mn), % 0.1 to 0.7
0
Nickel (Ni), % 0 to 0.0020
0 to 0.010
Silicon (Si), % 0 to 0.1
0
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 0
49.5 to 50.5
Zinc (Zn), % 0 to 0.2
0 to 0.0010
Residuals, % 0 to 0.010
0