EN-MC21210 Magnesium vs. SAE-AISI 1074 Steel

EN-MC21210 magnesium belongs to the magnesium alloys classification, while SAE-AISI 1074 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21210 magnesium and the bottom bar is SAE-AISI 1074 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 48
220 to 250
Elastic (Young's, Tensile) Modulus, GPa 44
190
Elongation at Break, % 14
11 to 14
Fatigue Strength, MPa 70
290 to 350
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
72
Shear Strength, MPa 110
440 to 490
Tensile Strength: Ultimate (UTS), MPa 190
740 to 820
Tensile Strength: Yield (Proof), MPa 90
450 to 570

Thermal Properties

Latent Heat of Fusion, J/g 350
250
Maximum Temperature: Mechanical, °C 100
400
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 570
1420
Specific Heat Capacity, J/kg-K 1000
470
Thermal Conductivity, W/m-K 120
50
Thermal Expansion, µm/m-K 27
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 130
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 12
1.8
Density, g/cm3 1.6
7.8
Embodied Carbon, kg CO2/kg material 24
1.4
Embodied Energy, MJ/kg 160
19
Embodied Water, L/kg 980
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 22
77 to 94
Resilience: Unit (Modulus of Resilience), kJ/m3 92
550 to 860
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 72
24
Strength to Weight: Axial, points 32
26 to 29
Strength to Weight: Bending, points 44
23 to 25
Thermal Diffusivity, mm2/s 76
14
Thermal Shock Resistance, points 11
24 to 26

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.6 to 2.6
0
Carbon (C), % 0
0.7 to 0.8
Copper (Cu), % 0 to 0.010
0
Iron (Fe), % 0 to 0.0050
98.3 to 98.8
Magnesium (Mg), % 96.3 to 98.3
0
Manganese (Mn), % 0.1 to 0.7
0.5 to 0.8
Nickel (Ni), % 0 to 0.0020
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.1
0
Sulfur (S), % 0
0 to 0.050
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.010
0