EN-MC21210 Magnesium vs. C11300 Copper

EN-MC21210 magnesium belongs to the magnesium alloys classification, while C11300 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21210 magnesium and the bottom bar is C11300 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
120
Elongation at Break, % 14
2.3 to 50
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 17
43
Shear Strength, MPa 110
160 to 240
Tensile Strength: Ultimate (UTS), MPa 190
230 to 410
Tensile Strength: Yield (Proof), MPa 90
77 to 400

Thermal Properties

Latent Heat of Fusion, J/g 350
210
Maximum Temperature: Mechanical, °C 100
200
Melting Completion (Liquidus), °C 600
1080
Melting Onset (Solidus), °C 570
1030
Specific Heat Capacity, J/kg-K 1000
390
Thermal Conductivity, W/m-K 120
390
Thermal Expansion, µm/m-K 27
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24
100
Electrical Conductivity: Equal Weight (Specific), % IACS 130
100

Otherwise Unclassified Properties

Base Metal Price, % relative 12
32
Density, g/cm3 1.6
9.0
Embodied Carbon, kg CO2/kg material 24
2.6
Embodied Energy, MJ/kg 160
42
Embodied Water, L/kg 980
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 22
8.5 to 91
Resilience: Unit (Modulus of Resilience), kJ/m3 92
25 to 690
Stiffness to Weight: Axial, points 15
7.2
Stiffness to Weight: Bending, points 72
18
Strength to Weight: Axial, points 32
7.2 to 13
Strength to Weight: Bending, points 44
9.4 to 14
Thermal Diffusivity, mm2/s 76
110
Thermal Shock Resistance, points 11
8.2 to 15

Alloy Composition

Aluminum (Al), % 1.6 to 2.6
0
Copper (Cu), % 0 to 0.010
99.85 to 99.973
Iron (Fe), % 0 to 0.0050
0
Magnesium (Mg), % 96.3 to 98.3
0
Manganese (Mn), % 0.1 to 0.7
0
Nickel (Ni), % 0 to 0.0020
0
Silicon (Si), % 0 to 0.1
0
Silver (Ag), % 0
0.027 to 0.050
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.010
0 to 0.1