EN-MC21210 Magnesium vs. C63800 Bronze

EN-MC21210 magnesium belongs to the magnesium alloys classification, while C63800 bronze belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21210 magnesium and the bottom bar is C63800 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
110
Elongation at Break, % 14
7.9 to 41
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 17
43
Shear Strength, MPa 110
320 to 500
Tensile Strength: Ultimate (UTS), MPa 190
460 to 1010

Thermal Properties

Latent Heat of Fusion, J/g 350
240
Maximum Temperature: Mechanical, °C 100
200
Melting Completion (Liquidus), °C 600
1030
Melting Onset (Solidus), °C 570
1000
Specific Heat Capacity, J/kg-K 1000
410
Thermal Conductivity, W/m-K 120
40
Thermal Expansion, µm/m-K 27
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24
10
Electrical Conductivity: Equal Weight (Specific), % IACS 130
10

Otherwise Unclassified Properties

Base Metal Price, % relative 12
30
Density, g/cm3 1.6
8.6
Embodied Carbon, kg CO2/kg material 24
2.8
Embodied Energy, MJ/kg 160
45
Embodied Water, L/kg 980
330

Common Calculations

Stiffness to Weight: Axial, points 15
7.4
Stiffness to Weight: Bending, points 72
19
Strength to Weight: Axial, points 32
15 to 33
Strength to Weight: Bending, points 44
15 to 26
Thermal Diffusivity, mm2/s 76
11
Thermal Shock Resistance, points 11
17 to 36

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.6 to 2.6
2.5 to 3.1
Cobalt (Co), % 0
0.25 to 0.55
Copper (Cu), % 0 to 0.010
92.4 to 95.8
Iron (Fe), % 0 to 0.0050
0 to 0.2
Lead (Pb), % 0
0 to 0.050
Magnesium (Mg), % 96.3 to 98.3
0
Manganese (Mn), % 0.1 to 0.7
0 to 0.1
Nickel (Ni), % 0 to 0.0020
0 to 0.2
Silicon (Si), % 0 to 0.1
1.5 to 2.1
Zinc (Zn), % 0 to 0.2
0 to 0.8
Residuals, % 0 to 0.010
0 to 0.5