EN-MC21210 Magnesium vs. C77400 Nickel Silver

EN-MC21210 magnesium belongs to the magnesium alloys classification, while C77400 nickel silver belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21210 magnesium and the bottom bar is C77400 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
110
Elongation at Break, % 14
25
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 17
42
Shear Strength, MPa 110
360
Tensile Strength: Ultimate (UTS), MPa 190
570
Tensile Strength: Yield (Proof), MPa 90
250

Thermal Properties

Latent Heat of Fusion, J/g 350
170
Maximum Temperature: Mechanical, °C 100
130
Melting Completion (Liquidus), °C 600
810
Melting Onset (Solidus), °C 570
770
Specific Heat Capacity, J/kg-K 1000
390
Thermal Expansion, µm/m-K 27
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24
27
Electrical Conductivity: Equal Weight (Specific), % IACS 130
31

Otherwise Unclassified Properties

Base Metal Price, % relative 12
25
Density, g/cm3 1.6
7.9
Embodied Carbon, kg CO2/kg material 24
3.5
Embodied Energy, MJ/kg 160
57
Embodied Water, L/kg 980
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 22
120
Resilience: Unit (Modulus of Resilience), kJ/m3 92
290
Stiffness to Weight: Axial, points 15
7.7
Stiffness to Weight: Bending, points 72
20
Strength to Weight: Axial, points 32
20
Strength to Weight: Bending, points 44
19
Thermal Shock Resistance, points 11
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.6 to 2.6
0
Copper (Cu), % 0 to 0.010
43 to 47
Iron (Fe), % 0 to 0.0050
0
Lead (Pb), % 0
0 to 0.2
Magnesium (Mg), % 96.3 to 98.3
0
Manganese (Mn), % 0.1 to 0.7
0
Nickel (Ni), % 0 to 0.0020
9.0 to 11
Silicon (Si), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.2
41.3 to 48
Residuals, % 0 to 0.010
0 to 0.5