EN-MC21230 Magnesium vs. Grade 14 Titanium

EN-MC21230 magnesium belongs to the magnesium alloys classification, while grade 14 titanium belongs to the titanium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21230 magnesium and the bottom bar is grade 14 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
110
Elongation at Break, % 10
23
Fatigue Strength, MPa 99
220
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 18
41
Shear Strength, MPa 130
290
Tensile Strength: Ultimate (UTS), MPa 220
460
Tensile Strength: Yield (Proof), MPa 140
310

Thermal Properties

Latent Heat of Fusion, J/g 350
420
Maximum Temperature: Mechanical, °C 120
320
Melting Completion (Liquidus), °C 600
1660
Melting Onset (Solidus), °C 520
1610
Specific Heat Capacity, J/kg-K 1000
540
Thermal Conductivity, W/m-K 72
21
Thermal Expansion, µm/m-K 27
8.7

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
3.4
Electrical Conductivity: Equal Weight (Specific), % IACS 63
6.9

Otherwise Unclassified Properties

Base Metal Price, % relative 12
37
Density, g/cm3 1.7
4.5
Embodied Carbon, kg CO2/kg material 23
32
Embodied Energy, MJ/kg 160
520
Embodied Water, L/kg 990
210

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19
93
Resilience: Unit (Modulus of Resilience), kJ/m3 200
450
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 71
35
Strength to Weight: Axial, points 36
28
Strength to Weight: Bending, points 48
29
Thermal Diffusivity, mm2/s 43
8.5
Thermal Shock Resistance, points 13
35

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 8.5
0
Carbon (C), % 0
0 to 0.080
Copper (Cu), % 0 to 0.010
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 0 to 0.0050
0 to 0.3
Magnesium (Mg), % 90.5 to 94.4
0
Manganese (Mn), % 0.1 to 0.6
0
Nickel (Ni), % 0 to 0.0020
0.4 to 0.6
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.15
Ruthenium (Ru), % 0
0.040 to 0.060
Silicon (Si), % 0 to 0.1
0
Titanium (Ti), % 0
98.4 to 99.56
Zinc (Zn), % 0 to 0.3
0
Residuals, % 0 to 0.010
0 to 0.4