MakeItFrom.com
Menu (ESC)

EN-MC21230 Magnesium vs. Grade 5 Titanium

EN-MC21230 magnesium belongs to the magnesium alloys classification, while grade 5 titanium belongs to the titanium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21230 magnesium and the bottom bar is grade 5 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
110
Elongation at Break, % 10
8.6 to 11
Fatigue Strength, MPa 99
530 to 630
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 18
40
Shear Strength, MPa 130
600 to 710
Tensile Strength: Ultimate (UTS), MPa 220
1000 to 1190
Tensile Strength: Yield (Proof), MPa 140
910 to 1110

Thermal Properties

Latent Heat of Fusion, J/g 350
410
Maximum Temperature: Mechanical, °C 120
330
Melting Completion (Liquidus), °C 600
1610
Melting Onset (Solidus), °C 520
1650
Specific Heat Capacity, J/kg-K 1000
560
Thermal Conductivity, W/m-K 72
6.8
Thermal Expansion, µm/m-K 27
8.9

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
1.0
Electrical Conductivity: Equal Weight (Specific), % IACS 63
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 12
36
Density, g/cm3 1.7
4.4
Embodied Carbon, kg CO2/kg material 23
38
Embodied Energy, MJ/kg 160
610
Embodied Water, L/kg 990
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19
100 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 200
3980 to 5880
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 71
35
Strength to Weight: Axial, points 36
62 to 75
Strength to Weight: Bending, points 48
50 to 56
Thermal Diffusivity, mm2/s 43
2.7
Thermal Shock Resistance, points 13
76 to 91

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 8.5
5.5 to 6.8
Carbon (C), % 0
0 to 0.080
Copper (Cu), % 0 to 0.010
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 0 to 0.0050
0 to 0.4
Magnesium (Mg), % 90.5 to 94.4
0
Manganese (Mn), % 0.1 to 0.6
0
Nickel (Ni), % 0 to 0.0020
0
Nitrogen (N), % 0
0 to 0.050
Oxygen (O), % 0
0 to 0.2
Silicon (Si), % 0 to 0.1
0
Titanium (Ti), % 0
87.4 to 91
Vanadium (V), % 0
3.5 to 4.5
Yttrium (Y), % 0
0 to 0.0050
Zinc (Zn), % 0 to 0.3
0
Residuals, % 0 to 0.010
0 to 0.4