EN-MC21230 Magnesium vs. C37100 Brass

EN-MC21230 magnesium belongs to the magnesium alloys classification, while C37100 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21230 magnesium and the bottom bar is C37100 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
100
Elongation at Break, % 10
8.0 to 40
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 18
40
Shear Strength, MPa 130
260 to 300
Tensile Strength: Ultimate (UTS), MPa 220
370 to 520
Tensile Strength: Yield (Proof), MPa 140
150 to 390

Thermal Properties

Latent Heat of Fusion, J/g 350
170
Maximum Temperature: Mechanical, °C 120
120
Melting Completion (Liquidus), °C 600
900
Melting Onset (Solidus), °C 520
890
Specific Heat Capacity, J/kg-K 1000
380
Thermal Conductivity, W/m-K 72
120
Thermal Expansion, µm/m-K 27
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
27
Electrical Conductivity: Equal Weight (Specific), % IACS 63
30

Otherwise Unclassified Properties

Base Metal Price, % relative 12
23
Density, g/cm3 1.7
8.0
Embodied Carbon, kg CO2/kg material 23
2.7
Embodied Energy, MJ/kg 160
45
Embodied Water, L/kg 990
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19
38 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 200
110 to 750
Stiffness to Weight: Axial, points 15
7.2
Stiffness to Weight: Bending, points 71
20
Strength to Weight: Axial, points 36
13 to 18
Strength to Weight: Bending, points 48
14 to 18
Thermal Diffusivity, mm2/s 43
39
Thermal Shock Resistance, points 13
12 to 17

Alloy Composition

Aluminum (Al), % 5.5 to 8.5
0
Copper (Cu), % 0 to 0.010
58 to 62
Iron (Fe), % 0 to 0.0050
0 to 0.15
Lead (Pb), % 0
0.6 to 1.2
Magnesium (Mg), % 90.5 to 94.4
0
Manganese (Mn), % 0.1 to 0.6
0
Nickel (Ni), % 0 to 0.0020
0
Silicon (Si), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.3
36.3 to 41.4
Residuals, % 0 to 0.010
0 to 0.4