EN-MC21310 Magnesium vs. B535.0 Aluminum

EN-MC21310 magnesium belongs to the magnesium alloys classification, while B535.0 aluminum belongs to the aluminum alloys.

For each property being compared, the top bar is EN-MC21310 magnesium and the bottom bar is B535.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 60
65
Elastic (Young's, Tensile) Modulus, GPa 45
66
Elongation at Break, % 9.0
10
Fatigue Strength, MPa 86
62
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 17
25
Shear Strength, MPa 120
210
Tensile Strength: Ultimate (UTS), MPa 200
260
Tensile Strength: Yield (Proof), MPa 120
130

Thermal Properties

Latent Heat of Fusion, J/g 360
390
Maximum Temperature: Mechanical, °C 100
170
Melting Completion (Liquidus), °C 600
630
Melting Onset (Solidus), °C 560
550
Specific Heat Capacity, J/kg-K 1000
910
Thermal Conductivity, W/m-K 89
96
Thermal Expansion, µm/m-K 26
25

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 22
24
Electrical Conductivity: Equal Weight (Specific), % IACS 120
82

Otherwise Unclassified Properties

Base Metal Price, % relative 12
9.5
Density, g/cm3 1.6
2.6
Embodied Carbon, kg CO2/kg material 23
9.4
Embodied Energy, MJ/kg 160
160
Embodied Water, L/kg 970
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 16
22
Resilience: Unit (Modulus of Resilience), kJ/m3 160
130
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 73
51
Strength to Weight: Axial, points 34
28
Strength to Weight: Bending, points 47
35
Thermal Diffusivity, mm2/s 55
40
Thermal Shock Resistance, points 12
11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.8 to 2.6
91.7 to 93.4
Copper (Cu), % 0 to 0.010
0 to 0.1
Iron (Fe), % 0 to 0.0050
0 to 0.15
Magnesium (Mg), % 95.2 to 97.4
6.5 to 7.5
Manganese (Mn), % 0.1 to 0.7
0 to 0.050
Nickel (Ni), % 0 to 0.0020
0
Silicon (Si), % 0.7 to 1.2
0 to 0.15
Titanium (Ti), % 0
0.1 to 0.25
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.010
0 to 0.15