EN-MC21310 Magnesium vs. C28500 Muntz Metal

EN-MC21310 magnesium belongs to the magnesium alloys classification, while C28500 Muntz Metal belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21310 magnesium and the bottom bar is C28500 Muntz Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
100
Elongation at Break, % 9.0
20
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 17
40
Shear Strength, MPa 120
320
Tensile Strength: Ultimate (UTS), MPa 200
520
Tensile Strength: Yield (Proof), MPa 120
380

Thermal Properties

Latent Heat of Fusion, J/g 360
170
Maximum Temperature: Mechanical, °C 100
110
Melting Completion (Liquidus), °C 600
900
Melting Onset (Solidus), °C 560
890
Specific Heat Capacity, J/kg-K 1000
390
Thermal Conductivity, W/m-K 89
100
Thermal Expansion, µm/m-K 26
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 22
29
Electrical Conductivity: Equal Weight (Specific), % IACS 120
33

Otherwise Unclassified Properties

Base Metal Price, % relative 12
22
Density, g/cm3 1.6
7.9
Embodied Carbon, kg CO2/kg material 23
2.7
Embodied Energy, MJ/kg 160
46
Embodied Water, L/kg 970
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 16
94
Resilience: Unit (Modulus of Resilience), kJ/m3 160
700
Stiffness to Weight: Axial, points 15
7.3
Stiffness to Weight: Bending, points 73
20
Strength to Weight: Axial, points 34
18
Strength to Weight: Bending, points 47
18
Thermal Diffusivity, mm2/s 55
33
Thermal Shock Resistance, points 12
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.8 to 2.6
0
Copper (Cu), % 0 to 0.010
57 to 59
Iron (Fe), % 0 to 0.0050
0 to 0.35
Lead (Pb), % 0
0 to 0.25
Magnesium (Mg), % 95.2 to 97.4
0
Manganese (Mn), % 0.1 to 0.7
0
Nickel (Ni), % 0 to 0.0020
0
Silicon (Si), % 0.7 to 1.2
0
Zinc (Zn), % 0 to 0.2
39.5 to 43
Residuals, % 0 to 0.010
0 to 0.9