EN-MC21310 Magnesium vs. C36000 Brass

EN-MC21310 magnesium belongs to the magnesium alloys classification, while C36000 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21310 magnesium and the bottom bar is C36000 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
100
Elongation at Break, % 9.0
5.8 to 23
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 17
39
Shear Strength, MPa 120
210 to 310
Tensile Strength: Ultimate (UTS), MPa 200
330 to 530
Tensile Strength: Yield (Proof), MPa 120
140 to 260

Thermal Properties

Latent Heat of Fusion, J/g 360
170
Maximum Temperature: Mechanical, °C 100
120
Melting Completion (Liquidus), °C 600
900
Melting Onset (Solidus), °C 560
890
Specific Heat Capacity, J/kg-K 1000
380
Thermal Conductivity, W/m-K 89
120
Thermal Expansion, µm/m-K 26
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 22
26
Electrical Conductivity: Equal Weight (Specific), % IACS 120
29

Otherwise Unclassified Properties

Base Metal Price, % relative 12
23
Density, g/cm3 1.6
8.2
Embodied Carbon, kg CO2/kg material 23
2.6
Embodied Energy, MJ/kg 160
45
Embodied Water, L/kg 970
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 16
25 to 62
Resilience: Unit (Modulus of Resilience), kJ/m3 160
89 to 340
Stiffness to Weight: Axial, points 15
7.0
Stiffness to Weight: Bending, points 73
19
Strength to Weight: Axial, points 34
11 to 18
Strength to Weight: Bending, points 47
13 to 18
Thermal Diffusivity, mm2/s 55
37
Thermal Shock Resistance, points 12
11 to 18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.8 to 2.6
0
Copper (Cu), % 0 to 0.010
60 to 63
Iron (Fe), % 0 to 0.0050
0 to 0.35
Lead (Pb), % 0
2.5 to 3.7
Magnesium (Mg), % 95.2 to 97.4
0
Manganese (Mn), % 0.1 to 0.7
0
Nickel (Ni), % 0 to 0.0020
0
Silicon (Si), % 0.7 to 1.2
0
Zinc (Zn), % 0 to 0.2
32.5 to 37.5
Residuals, % 0 to 0.010
0 to 0.5