EN-MC21310 Magnesium vs. C53400 Bronze

EN-MC21310 magnesium belongs to the magnesium alloys classification, while C53400 bronze belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21310 magnesium and the bottom bar is C53400 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
110
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 17
42
Tensile Strength: Ultimate (UTS), MPa 200
330 to 720

Thermal Properties

Latent Heat of Fusion, J/g 360
200
Maximum Temperature: Mechanical, °C 100
180
Melting Completion (Liquidus), °C 600
1050
Melting Onset (Solidus), °C 560
950
Specific Heat Capacity, J/kg-K 1000
380
Thermal Conductivity, W/m-K 89
69
Thermal Expansion, µm/m-K 26
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 22
15
Electrical Conductivity: Equal Weight (Specific), % IACS 120
15

Otherwise Unclassified Properties

Base Metal Price, % relative 12
32
Density, g/cm3 1.6
8.9
Embodied Carbon, kg CO2/kg material 23
3.0
Embodied Energy, MJ/kg 160
49
Embodied Water, L/kg 970
350

Common Calculations

Stiffness to Weight: Axial, points 15
7.0
Stiffness to Weight: Bending, points 73
18
Strength to Weight: Axial, points 34
10 to 22
Strength to Weight: Bending, points 47
12 to 20
Thermal Diffusivity, mm2/s 55
21
Thermal Shock Resistance, points 12
12 to 26

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.8 to 2.6
0
Copper (Cu), % 0 to 0.010
91.8 to 95.7
Iron (Fe), % 0 to 0.0050
0 to 0.1
Lead (Pb), % 0
0.8 to 1.2
Magnesium (Mg), % 95.2 to 97.4
0
Manganese (Mn), % 0.1 to 0.7
0
Nickel (Ni), % 0 to 0.0020
0
Phosphorus (P), % 0
0.030 to 0.35
Silicon (Si), % 0.7 to 1.2
0
Tin (Sn), % 0
3.5 to 5.8
Zinc (Zn), % 0 to 0.2
0 to 0.3
Residuals, % 0 to 0.010
0 to 0.5