EN-MC21310 Magnesium vs. C86100 Bronze

EN-MC21310 magnesium belongs to the magnesium alloys classification, while C86100 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21310 magnesium and the bottom bar is C86100 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
110
Elongation at Break, % 9.0
20
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 17
43
Tensile Strength: Ultimate (UTS), MPa 200
660
Tensile Strength: Yield (Proof), MPa 120
350

Thermal Properties

Latent Heat of Fusion, J/g 360
200
Maximum Temperature: Mechanical, °C 100
170
Melting Completion (Liquidus), °C 600
940
Melting Onset (Solidus), °C 560
900
Specific Heat Capacity, J/kg-K 1000
420
Thermal Conductivity, W/m-K 89
35
Thermal Expansion, µm/m-K 26
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 22
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 120
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 12
24
Density, g/cm3 1.6
8.0
Embodied Carbon, kg CO2/kg material 23
2.9
Embodied Energy, MJ/kg 160
49
Embodied Water, L/kg 970
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 16
110
Resilience: Unit (Modulus of Resilience), kJ/m3 160
530
Stiffness to Weight: Axial, points 15
7.8
Stiffness to Weight: Bending, points 73
20
Strength to Weight: Axial, points 34
23
Strength to Weight: Bending, points 47
21
Thermal Diffusivity, mm2/s 55
10
Thermal Shock Resistance, points 12
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.8 to 2.6
4.5 to 5.5
Copper (Cu), % 0 to 0.010
66 to 68
Iron (Fe), % 0 to 0.0050
2.0 to 4.0
Lead (Pb), % 0
0 to 0.1
Magnesium (Mg), % 95.2 to 97.4
0
Manganese (Mn), % 0.1 to 0.7
2.5 to 5.0
Nickel (Ni), % 0 to 0.0020
0
Silicon (Si), % 0.7 to 1.2
0
Tin (Sn), % 0
0 to 0.1
Zinc (Zn), % 0 to 0.2
17.3 to 25
Residuals, % 0 to 0.010
0