EN-MC21310 Magnesium vs. C92600 Bronze

EN-MC21310 magnesium belongs to the magnesium alloys classification, while C92600 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21310 magnesium and the bottom bar is C92600 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 60
70
Elastic (Young's, Tensile) Modulus, GPa 45
110
Elongation at Break, % 9.0
30
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 17
40
Tensile Strength: Ultimate (UTS), MPa 200
300
Tensile Strength: Yield (Proof), MPa 120
140

Thermal Properties

Latent Heat of Fusion, J/g 360
190
Maximum Temperature: Mechanical, °C 100
170
Melting Completion (Liquidus), °C 600
980
Melting Onset (Solidus), °C 560
840
Specific Heat Capacity, J/kg-K 1000
370
Thermal Conductivity, W/m-K 89
67
Thermal Expansion, µm/m-K 26
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 22
9.0
Electrical Conductivity: Equal Weight (Specific), % IACS 120
9.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
34
Density, g/cm3 1.6
8.7
Embodied Carbon, kg CO2/kg material 23
3.6
Embodied Energy, MJ/kg 160
58
Embodied Water, L/kg 970
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 16
74
Resilience: Unit (Modulus of Resilience), kJ/m3 160
88
Stiffness to Weight: Axial, points 15
6.8
Stiffness to Weight: Bending, points 73
18
Strength to Weight: Axial, points 34
9.6
Strength to Weight: Bending, points 47
11
Thermal Diffusivity, mm2/s 55
21
Thermal Shock Resistance, points 12
11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.8 to 2.6
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Copper (Cu), % 0 to 0.010
86 to 88.5
Iron (Fe), % 0 to 0.0050
0 to 0.2
Lead (Pb), % 0
0.8 to 1.5
Magnesium (Mg), % 95.2 to 97.4
0
Manganese (Mn), % 0.1 to 0.7
0
Nickel (Ni), % 0 to 0.0020
0 to 0.7
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0.7 to 1.2
0 to 0.0050
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0
9.3 to 10.5
Zinc (Zn), % 0 to 0.2
1.3 to 2.5
Residuals, % 0 to 0.010
0 to 0.7