EN-MC21310 Magnesium vs. C93600 Bronze

EN-MC21310 magnesium belongs to the magnesium alloys classification, while C93600 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21310 magnesium and the bottom bar is C93600 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
99
Elongation at Break, % 9.0
14
Poisson's Ratio 0.29
0.35
Shear Modulus, GPa 17
36
Tensile Strength: Ultimate (UTS), MPa 200
260
Tensile Strength: Yield (Proof), MPa 120
140

Thermal Properties

Latent Heat of Fusion, J/g 360
170
Maximum Temperature: Mechanical, °C 100
150
Melting Completion (Liquidus), °C 600
940
Melting Onset (Solidus), °C 560
840
Specific Heat Capacity, J/kg-K 1000
350
Thermal Conductivity, W/m-K 89
49
Thermal Expansion, µm/m-K 26
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 22
11
Electrical Conductivity: Equal Weight (Specific), % IACS 120
11

Otherwise Unclassified Properties

Base Metal Price, % relative 12
31
Density, g/cm3 1.6
9.0
Embodied Carbon, kg CO2/kg material 23
3.2
Embodied Energy, MJ/kg 160
51
Embodied Water, L/kg 970
370

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 16
31
Resilience: Unit (Modulus of Resilience), kJ/m3 160
98
Stiffness to Weight: Axial, points 15
6.1
Stiffness to Weight: Bending, points 73
17
Strength to Weight: Axial, points 34
7.9
Strength to Weight: Bending, points 47
9.9
Thermal Diffusivity, mm2/s 55
16
Thermal Shock Resistance, points 12
9.8

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.8 to 2.6
0 to 0.0050
Antimony (Sb), % 0
0 to 0.55
Copper (Cu), % 0 to 0.010
79 to 83
Iron (Fe), % 0 to 0.0050
0 to 0.2
Lead (Pb), % 0
11 to 13
Magnesium (Mg), % 95.2 to 97.4
0
Manganese (Mn), % 0.1 to 0.7
0
Nickel (Ni), % 0 to 0.0020
0 to 1.0
Phosphorus (P), % 0
0 to 1.5
Silicon (Si), % 0.7 to 1.2
0 to 0.0050
Sulfur (S), % 0
0 to 0.080
Tin (Sn), % 0
6.0 to 8.0
Zinc (Zn), % 0 to 0.2
0 to 1.0
Residuals, % 0 to 0.010
0 to 0.7