EN-MC21310 Magnesium vs. ZA-27

EN-MC21310 magnesium belongs to the magnesium alloys classification, while ZA-27 belongs to the zinc alloys. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21310 magnesium and the bottom bar is ZA-27.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 60
100 to 120
Elastic (Young's, Tensile) Modulus, GPa 45
78
Elongation at Break, % 9.0
2.0 to 4.5
Fatigue Strength, MPa 86
110 to 170
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 17
31
Shear Strength, MPa 120
230 to 330
Tensile Strength: Ultimate (UTS), MPa 200
400 to 430
Tensile Strength: Yield (Proof), MPa 120
260 to 370

Thermal Properties

Latent Heat of Fusion, J/g 360
130
Maximum Temperature: Mechanical, °C 100
120
Melting Completion (Liquidus), °C 600
480
Melting Onset (Solidus), °C 560
380
Specific Heat Capacity, J/kg-K 1000
530
Thermal Conductivity, W/m-K 89
130
Thermal Expansion, µm/m-K 26
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 22
30
Electrical Conductivity: Equal Weight (Specific), % IACS 120
53

Otherwise Unclassified Properties

Base Metal Price, % relative 12
11
Density, g/cm3 1.6
5.0
Embodied Carbon, kg CO2/kg material 23
4.2
Embodied Energy, MJ/kg 160
80
Embodied Water, L/kg 970
570

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 16
8.1 to 18
Resilience: Unit (Modulus of Resilience), kJ/m3 160
420 to 890
Stiffness to Weight: Axial, points 15
8.6
Stiffness to Weight: Bending, points 73
28
Strength to Weight: Axial, points 34
22 to 24
Strength to Weight: Bending, points 47
24 to 25
Thermal Diffusivity, mm2/s 55
47
Thermal Shock Resistance, points 12
14 to 15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.8 to 2.6
25 to 28
Cadmium (Cd), % 0
0 to 0.0060
Copper (Cu), % 0 to 0.010
2.0 to 2.5
Iron (Fe), % 0 to 0.0050
0 to 0.1
Lead (Pb), % 0
0 to 0.0060
Magnesium (Mg), % 95.2 to 97.4
0.010 to 0.020
Manganese (Mn), % 0.1 to 0.7
0
Nickel (Ni), % 0 to 0.0020
0 to 0.020
Silicon (Si), % 0.7 to 1.2
0 to 0.080
Tin (Sn), % 0
0 to 0.0030
Zinc (Zn), % 0 to 0.2
69.3 to 73
Residuals, % 0 to 0.010
0