EN-MC21320 Magnesium vs. AWS BAg-10

EN-MC21320 magnesium belongs to the magnesium alloys classification, while AWS BAg-10 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21320 magnesium and the bottom bar is AWS BAg-10.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
82
Poisson's Ratio 0.29
0.35
Shear Modulus, GPa 18
30
Tensile Strength: Ultimate (UTS), MPa 230
140

Thermal Properties

Latent Heat of Fusion, J/g 370
130
Melting Completion (Liquidus), °C 600
740
Melting Onset (Solidus), °C 530
690
Specific Heat Capacity, J/kg-K 1000
280
Thermal Expansion, µm/m-K 26
20

Otherwise Unclassified Properties

Density, g/cm3 1.6
9.8

Common Calculations

Stiffness to Weight: Axial, points 15
4.6
Stiffness to Weight: Bending, points 72
15
Strength to Weight: Axial, points 38
4.0
Strength to Weight: Bending, points 50
6.1
Thermal Shock Resistance, points 13
6.2

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 3.5 to 5.0
0
Copper (Cu), % 0 to 0.010
19 to 21
Iron (Fe), % 0 to 0.0050
0
Magnesium (Mg), % 92.5 to 95.9
0
Manganese (Mn), % 0.1 to 0.7
0
Nickel (Ni), % 0 to 0.0020
0
Silicon (Si), % 0.5 to 1.5
0
Silver (Ag), % 0
69 to 71
Zinc (Zn), % 0 to 0.2
8.0 to 12
Residuals, % 0 to 0.010
0 to 0.15