EN-MC21320 Magnesium vs. AWS E310Mo

EN-MC21320 magnesium belongs to the magnesium alloys classification, while AWS E310Mo belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21320 magnesium and the bottom bar is AWS E310Mo.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
200
Elongation at Break, % 7.5
34
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 18
80
Tensile Strength: Ultimate (UTS), MPa 230
620

Thermal Properties

Latent Heat of Fusion, J/g 370
310
Melting Completion (Liquidus), °C 600
1420
Melting Onset (Solidus), °C 530
1370
Specific Heat Capacity, J/kg-K 1000
470
Thermal Conductivity, W/m-K 66
14
Thermal Expansion, µm/m-K 26
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 17
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 91
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 12
28
Density, g/cm3 1.6
7.9
Embodied Carbon, kg CO2/kg material 23
5.1
Embodied Energy, MJ/kg 160
71
Embodied Water, L/kg 980
210

Common Calculations

Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 72
25
Strength to Weight: Axial, points 38
22
Strength to Weight: Bending, points 50
20
Thermal Diffusivity, mm2/s 40
3.7
Thermal Shock Resistance, points 13
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 3.5 to 5.0
0
Carbon (C), % 0
0 to 0.12
Chromium (Cr), % 0
25 to 28
Copper (Cu), % 0 to 0.010
0 to 0.75
Iron (Fe), % 0 to 0.0050
42.8 to 52
Magnesium (Mg), % 92.5 to 95.9
0
Manganese (Mn), % 0.1 to 0.7
1.0 to 2.5
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 0 to 0.0020
20 to 22
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0.5 to 1.5
0 to 0.75
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.010
0