EN-MC21320 Magnesium vs. EN 1.7323 Steel

EN-MC21320 magnesium belongs to the magnesium alloys classification, while EN 1.7323 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21320 magnesium and the bottom bar is EN 1.7323 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 68
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 45
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 18
73
Tensile Strength: Ultimate (UTS), MPa 230
480 to 1460

Thermal Properties

Latent Heat of Fusion, J/g 370
250
Maximum Temperature: Mechanical, °C 110
410
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 530
1420
Specific Heat Capacity, J/kg-K 1000
470
Thermal Conductivity, W/m-K 66
45
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 17
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 91
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.5
Density, g/cm3 1.6
7.9
Embodied Carbon, kg CO2/kg material 23
1.5
Embodied Energy, MJ/kg 160
20
Embodied Water, L/kg 980
50

Common Calculations

Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 72
24
Strength to Weight: Axial, points 38
17 to 52
Strength to Weight: Bending, points 50
17 to 36
Thermal Diffusivity, mm2/s 40
12
Thermal Shock Resistance, points 13
14 to 43

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 3.5 to 5.0
0
Carbon (C), % 0
0.17 to 0.23
Chromium (Cr), % 0
0.3 to 0.6
Copper (Cu), % 0 to 0.010
0 to 0.25
Iron (Fe), % 0 to 0.0050
97.1 to 98.4
Magnesium (Mg), % 92.5 to 95.9
0
Manganese (Mn), % 0.1 to 0.7
0.7 to 1.0
Molybdenum (Mo), % 0
0.4 to 0.5
Nickel (Ni), % 0 to 0.0020
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0.5 to 1.5
0 to 0.3
Sulfur (S), % 0
0.020 to 0.040
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.010
0