EN-MC21320 Magnesium vs. Solder Alloy 151

EN-MC21320 magnesium belongs to the magnesium alloys classification, while solder alloy 151 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21320 magnesium and the bottom bar is solder alloy 151.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
39
Elongation at Break, % 7.5
37
Poisson's Ratio 0.29
0.37
Shear Modulus, GPa 18
14
Tensile Strength: Ultimate (UTS), MPa 230
46

Thermal Properties

Latent Heat of Fusion, J/g 370
47
Melting Completion (Liquidus), °C 600
150
Melting Onset (Solidus), °C 530
150
Specific Heat Capacity, J/kg-K 1000
190
Thermal Conductivity, W/m-K 66
44
Thermal Expansion, µm/m-K 26
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 17
10
Electrical Conductivity: Equal Weight (Specific), % IACS 91
10

Otherwise Unclassified Properties

Density, g/cm3 1.6
8.8
Embodied Carbon, kg CO2/kg material 23
9.2
Embodied Energy, MJ/kg 160
160
Embodied Water, L/kg 980
920

Common Calculations

Stiffness to Weight: Axial, points 15
2.5
Stiffness to Weight: Bending, points 72
13
Strength to Weight: Axial, points 38
1.4
Strength to Weight: Bending, points 50
3.2
Thermal Diffusivity, mm2/s 40
26
Thermal Shock Resistance, points 13
3.2

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 3.5 to 5.0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
17.5 to 18.5
Copper (Cu), % 0 to 0.010
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.0050
0 to 0.020
Lead (Pb), % 0
30.3 to 33
Magnesium (Mg), % 92.5 to 95.9
0
Manganese (Mn), % 0.1 to 0.7
0
Nickel (Ni), % 0 to 0.0020
0 to 0.010
Silicon (Si), % 0.5 to 1.5
0
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 0
49.5 to 50.5
Zinc (Zn), % 0 to 0.2
0 to 0.0010
Residuals, % 0 to 0.010
0