EN-MC21320 Magnesium vs. C77000 Nickel Silver

EN-MC21320 magnesium belongs to the magnesium alloys classification, while C77000 nickel silver belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21320 magnesium and the bottom bar is C77000 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
120
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 18
46
Tensile Strength: Ultimate (UTS), MPa 230
420 to 800

Thermal Properties

Latent Heat of Fusion, J/g 370
200
Maximum Temperature: Mechanical, °C 110
180
Melting Completion (Liquidus), °C 600
1050
Melting Onset (Solidus), °C 530
1000
Specific Heat Capacity, J/kg-K 1000
400
Thermal Conductivity, W/m-K 66
29
Thermal Expansion, µm/m-K 26
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 17
5.5
Electrical Conductivity: Equal Weight (Specific), % IACS 91
6.0

Otherwise Unclassified Properties

Base Metal Price, % relative 12
31
Density, g/cm3 1.6
8.3
Embodied Carbon, kg CO2/kg material 23
4.1
Embodied Energy, MJ/kg 160
63
Embodied Water, L/kg 980
300

Common Calculations

Stiffness to Weight: Axial, points 15
8.1
Stiffness to Weight: Bending, points 72
20
Strength to Weight: Axial, points 38
14 to 27
Strength to Weight: Bending, points 50
15 to 23
Thermal Diffusivity, mm2/s 40
8.8
Thermal Shock Resistance, points 13
15 to 28

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 3.5 to 5.0
0
Copper (Cu), % 0 to 0.010
53.5 to 56.5
Iron (Fe), % 0 to 0.0050
0 to 0.25
Lead (Pb), % 0
0 to 0.050
Magnesium (Mg), % 92.5 to 95.9
0
Manganese (Mn), % 0.1 to 0.7
0 to 0.5
Nickel (Ni), % 0 to 0.0020
16.5 to 19.5
Silicon (Si), % 0.5 to 1.5
0
Zinc (Zn), % 0 to 0.2
22.7 to 30
Residuals, % 0 to 0.010
0 to 0.5