EN-MC21320 Magnesium vs. R05400 Tantalum

EN-MC21320 magnesium belongs to the magnesium alloys classification, while R05400 tantalum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21320 magnesium and the bottom bar is R05400 tantalum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
190
Elongation at Break, % 7.5
1.1 to 28
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 18
69
Tensile Strength: Ultimate (UTS), MPa 230
210 to 540
Tensile Strength: Yield (Proof), MPa 140
140 to 390

Thermal Properties

Latent Heat of Fusion, J/g 370
140
Specific Heat Capacity, J/kg-K 1000
140
Thermal Conductivity, W/m-K 66
59
Thermal Expansion, µm/m-K 26
6.5

Otherwise Unclassified Properties

Density, g/cm3 1.6
17
Embodied Water, L/kg 980
650

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 15
5.5 to 53
Resilience: Unit (Modulus of Resilience), kJ/m3 200
50 to 420
Stiffness to Weight: Axial, points 15
6.2
Stiffness to Weight: Bending, points 72
11
Strength to Weight: Axial, points 38
3.6 to 9.0
Strength to Weight: Bending, points 50
4.8 to 8.8
Thermal Diffusivity, mm2/s 40
25
Thermal Shock Resistance, points 13
13 to 32

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 3.5 to 5.0
0
Carbon (C), % 0
0 to 0.010
Copper (Cu), % 0 to 0.010
0
Hydrogen (H), % 0
0 to 0.0015
Iron (Fe), % 0 to 0.0050
0 to 0.010
Magnesium (Mg), % 92.5 to 95.9
0
Manganese (Mn), % 0.1 to 0.7
0
Molybdenum (Mo), % 0
0 to 0.020
Nickel (Ni), % 0 to 0.0020
0 to 0.010
Niobium (Nb), % 0
0 to 0.1
Nitrogen (N), % 0
0 to 0.010
Oxygen (O), % 0
0 to 0.030
Silicon (Si), % 0.5 to 1.5
0 to 0.0050
Tantalum (Ta), % 0
99.7 to 100
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
0 to 0.050
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.010
0