EN-MC32110 Magnesium vs. AWS BAg-22

EN-MC32110 magnesium belongs to the magnesium alloys classification, while AWS BAg-22 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC32110 magnesium and the bottom bar is AWS BAg-22.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 49
96
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 19
36
Tensile Strength: Ultimate (UTS), MPa 220
140

Thermal Properties

Latent Heat of Fusion, J/g 330
150
Melting Completion (Liquidus), °C 600
700
Melting Onset (Solidus), °C 500
680
Specific Heat Capacity, J/kg-K 950
320
Thermal Expansion, µm/m-K 26
21

Otherwise Unclassified Properties

Density, g/cm3 2.1
9.0
Embodied Carbon, kg CO2/kg material 22
48
Embodied Energy, MJ/kg 150
760

Common Calculations

Stiffness to Weight: Axial, points 13
5.9
Stiffness to Weight: Bending, points 58
17
Strength to Weight: Axial, points 29
4.3
Strength to Weight: Bending, points 38
6.6
Thermal Shock Resistance, points 12
5.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.2
0
Copper (Cu), % 2.4 to 3.0
15 to 17
Iron (Fe), % 0 to 0.050
0
Magnesium (Mg), % 89.3 to 91.9
0
Manganese (Mn), % 0.25 to 0.75
7.0 to 8.0
Nickel (Ni), % 0 to 0.010
4.0 to 5.0
Silicon (Si), % 0 to 0.2
0
Silver (Ag), % 0
48 to 50
Zinc (Zn), % 5.5 to 6.5
21 to 25
Residuals, % 0 to 0.010
0 to 0.15