EN-MC32110 Magnesium vs. EN 1.0920 Steel

EN-MC32110 magnesium belongs to the magnesium alloys classification, while EN 1.0920 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC32110 magnesium and the bottom bar is EN 1.0920 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 60
160
Elastic (Young's, Tensile) Modulus, GPa 49
190
Elongation at Break, % 2.2
23
Fatigue Strength, MPa 80
270
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 19
73
Shear Strength, MPa 120
340
Tensile Strength: Ultimate (UTS), MPa 220
540
Tensile Strength: Yield (Proof), MPa 140
380

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 99
400
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 500
1420
Specific Heat Capacity, J/kg-K 950
470
Thermal Conductivity, W/m-K 120
50
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 32
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 140
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 13
2.4
Density, g/cm3 2.1
7.8
Embodied Carbon, kg CO2/kg material 22
1.6
Embodied Energy, MJ/kg 150
22
Embodied Water, L/kg 920
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 4.3
110
Resilience: Unit (Modulus of Resilience), kJ/m3 210
380
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 58
24
Strength to Weight: Axial, points 29
19
Strength to Weight: Bending, points 38
19
Thermal Diffusivity, mm2/s 58
14
Thermal Shock Resistance, points 12
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.2
0.020 to 0.060
Carbon (C), % 0
0 to 0.2
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 2.4 to 3.0
0 to 0.35
Iron (Fe), % 0 to 0.050
96.1 to 99.08
Magnesium (Mg), % 89.3 to 91.9
0
Manganese (Mn), % 0.25 to 0.75
0.9 to 1.7
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 0 to 0.010
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 0.2
0 to 0.5
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.12
Zinc (Zn), % 5.5 to 6.5
0
Residuals, % 0 to 0.010
0