EN-MC32110 Magnesium vs. Solder Alloy 182

EN-MC32110 magnesium belongs to the magnesium alloys classification, while solder alloy 182 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC32110 magnesium and the bottom bar is solder alloy 182.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 49
19
Elongation at Break, % 2.2
37
Poisson's Ratio 0.29
0.44
Shear Modulus, GPa 19
6.7
Tensile Strength: Ultimate (UTS), MPa 220
28

Thermal Properties

Latent Heat of Fusion, J/g 330
28
Melting Completion (Liquidus), °C 600
370
Melting Onset (Solidus), °C 500
300
Specific Heat Capacity, J/kg-K 950
130
Thermal Conductivity, W/m-K 120
27
Thermal Expansion, µm/m-K 26
29

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 32
9.6
Electrical Conductivity: Equal Weight (Specific), % IACS 140
7.6

Otherwise Unclassified Properties

Density, g/cm3 2.1
11
Embodied Carbon, kg CO2/kg material 22
9.0
Embodied Energy, MJ/kg 150
140

Common Calculations

Stiffness to Weight: Axial, points 13
0.95
Stiffness to Weight: Bending, points 58
7.9
Strength to Weight: Axial, points 29
0.69
Strength to Weight: Bending, points 38
1.8
Thermal Diffusivity, mm2/s 58
18
Thermal Shock Resistance, points 12
3.7

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.2
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Copper (Cu), % 2.4 to 3.0
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.050
0 to 0.020
Lead (Pb), % 0
93.2 to 95
Magnesium (Mg), % 89.3 to 91.9
0
Manganese (Mn), % 0.25 to 0.75
0
Nickel (Ni), % 0 to 0.010
0 to 0.010
Silicon (Si), % 0 to 0.2
0
Silver (Ag), % 0
5.0 to 6.0
Tin (Sn), % 0
0 to 0.25
Zinc (Zn), % 5.5 to 6.5
0 to 0.0010
Residuals, % 0 to 0.010
0