EN-MC32110 Magnesium vs. R60802 Alloy

EN-MC32110 magnesium belongs to the magnesium alloys classification, while R60802 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC32110 magnesium and the bottom bar is R60802 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 49
98
Elongation at Break, % 2.2
22
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 19
36
Tensile Strength: Ultimate (UTS), MPa 220
430
Tensile Strength: Yield (Proof), MPa 140
270

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Specific Heat Capacity, J/kg-K 950
270
Thermal Conductivity, W/m-K 120
22
Thermal Expansion, µm/m-K 26
6.0

Otherwise Unclassified Properties

Density, g/cm3 2.1
6.5
Embodied Water, L/kg 920
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 4.3
85
Resilience: Unit (Modulus of Resilience), kJ/m3 210
380
Stiffness to Weight: Axial, points 13
8.3
Stiffness to Weight: Bending, points 58
23
Strength to Weight: Axial, points 29
18
Strength to Weight: Bending, points 38
19
Thermal Diffusivity, mm2/s 58
12
Thermal Shock Resistance, points 12
53

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.2
0
Chromium (Cr), % 0
0.050 to 0.15
Copper (Cu), % 2.4 to 3.0
0
Iron (Fe), % 0 to 0.050
0.070 to 0.2
Magnesium (Mg), % 89.3 to 91.9
0
Manganese (Mn), % 0.25 to 0.75
0
Nickel (Ni), % 0 to 0.010
0.030 to 0.080
Silicon (Si), % 0 to 0.2
0
Tin (Sn), % 0
1.2 to 1.7
Zinc (Zn), % 5.5 to 6.5
0
Zirconium (Zr), % 0
97.8 to 98.7
Residuals, % 0 to 0.010
0 to 0.11