EN-MC35110 Magnesium vs. 1060 Aluminum

EN-MC35110 magnesium belongs to the magnesium alloys classification, while 1060 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN-MC35110 magnesium and the bottom bar is 1060 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
68
Elongation at Break, % 3.1
1.1 to 30
Fatigue Strength, MPa 110
15 to 50
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 18
26
Shear Strength, MPa 130
42 to 75
Tensile Strength: Ultimate (UTS), MPa 230
67 to 130
Tensile Strength: Yield (Proof), MPa 150
17 to 110

Thermal Properties

Latent Heat of Fusion, J/g 330
400
Maximum Temperature: Mechanical, °C 140
170
Melting Completion (Liquidus), °C 600
660
Melting Onset (Solidus), °C 520
650
Specific Heat Capacity, J/kg-K 970
900
Thermal Conductivity, W/m-K 110
230
Thermal Expansion, µm/m-K 26
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
62
Electrical Conductivity: Equal Weight (Specific), % IACS 130
210

Otherwise Unclassified Properties

Base Metal Price, % relative 18
9.5
Density, g/cm3 1.9
2.7
Embodied Carbon, kg CO2/kg material 24
8.3
Embodied Energy, MJ/kg 170
160
Embodied Water, L/kg 940
1200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.3
0.57 to 37
Resilience: Unit (Modulus of Resilience), kJ/m3 260
2.1 to 89
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 63
50
Strength to Weight: Axial, points 34
6.9 to 13
Strength to Weight: Bending, points 44
14 to 21
Thermal Diffusivity, mm2/s 61
96
Thermal Shock Resistance, points 14
3.0 to 5.6

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
99.6 to 100
Copper (Cu), % 0 to 0.030
0 to 0.050
Iron (Fe), % 0 to 0.010
0 to 0.35
Magnesium (Mg), % 92 to 95.4
0 to 0.030
Manganese (Mn), % 0 to 0.15
0 to 0.030
Nickel (Ni), % 0 to 0.0050
0
Silicon (Si), % 0 to 0.010
0 to 0.25
Titanium (Ti), % 0
0 to 0.030
Unspecified Rare Earths, % 0.75 to 1.8
0
Vanadium (V), % 0
0 to 0.050
Zinc (Zn), % 3.5 to 5.0
0 to 0.050
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0