MakeItFrom.com
Menu (ESC)

EN-MC35110 Magnesium vs. EN 1.7230 Steel

EN-MC35110 magnesium belongs to the magnesium alloys classification, while EN 1.7230 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC35110 magnesium and the bottom bar is EN 1.7230 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 63
220 to 270
Elastic (Young's, Tensile) Modulus, GPa 45
190
Elongation at Break, % 3.1
11 to 12
Fatigue Strength, MPa 110
320 to 460
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 18
73
Tensile Strength: Ultimate (UTS), MPa 230
720 to 910
Tensile Strength: Yield (Proof), MPa 150
510 to 740

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 140
420
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 520
1420
Specific Heat Capacity, J/kg-K 970
470
Thermal Conductivity, W/m-K 110
44
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 130
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 18
2.4
Density, g/cm3 1.9
7.8
Embodied Carbon, kg CO2/kg material 24
1.5
Embodied Energy, MJ/kg 170
20
Embodied Water, L/kg 940
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.3
79 to 97
Resilience: Unit (Modulus of Resilience), kJ/m3 260
700 to 1460
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 63
24
Strength to Weight: Axial, points 34
26 to 32
Strength to Weight: Bending, points 44
23 to 27
Thermal Diffusivity, mm2/s 61
12
Thermal Shock Resistance, points 14
21 to 27

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.3 to 0.37
Chromium (Cr), % 0
0.8 to 1.2
Copper (Cu), % 0 to 0.030
0
Iron (Fe), % 0 to 0.010
96.7 to 98.3
Magnesium (Mg), % 92 to 95.4
0
Manganese (Mn), % 0 to 0.15
0.5 to 0.8
Molybdenum (Mo), % 0
0.15 to 0.3
Nickel (Ni), % 0 to 0.0050
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.010
0 to 0.6
Sulfur (S), % 0
0 to 0.030
Unspecified Rare Earths, % 0.75 to 1.8
0
Zinc (Zn), % 3.5 to 5.0
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0