EN-MC65210 Magnesium vs. 6016 Aluminum
EN-MC65210 magnesium belongs to the magnesium alloys classification, while 6016 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN-MC65210 magnesium and the bottom bar is 6016 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 80 | |
| 55 to 80 |
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 69 |
| Elongation at Break, % | 2.8 | |
| 11 to 27 |
| Fatigue Strength, MPa | 110 | |
| 68 to 89 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 17 | |
| 26 |
| Shear Strength, MPa | 150 | |
| 130 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 270 | |
| 200 to 280 |
| Tensile Strength: Yield (Proof), MPa | 200 | |
| 110 to 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 160 |
| Melting Completion (Liquidus), °C | 610 | |
| 660 |
| Melting Onset (Solidus), °C | 540 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 970 | |
| 900 |
| Thermal Conductivity, W/m-K | 110 | |
| 190 to 210 |
| Thermal Expansion, µm/m-K | 26 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 48 to 54 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 160 to 180 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.0 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 27 | |
| 8.2 |
| Embodied Energy, MJ/kg | 220 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.9 | |
| 29 to 47 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 450 | |
| 82 to 340 |
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 59 | |
| 51 |
| Strength to Weight: Axial, points | 38 | |
| 21 to 29 |
| Strength to Weight: Bending, points | 47 | |
| 29 to 35 |
| Thermal Diffusivity, mm2/s | 58 | |
| 77 to 86 |
| Thermal Shock Resistance, points | 17 | |
| 9.1 to 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 96.4 to 98.8 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.030 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 92.6 to 95.6 | |
| 0.25 to 0.6 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 |
| Silicon (Si), % | 0 to 0.010 | |
| 1.0 to 1.5 |
| Silver (Ag), % | 2.0 to 3.0 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.15 |
| Unspecified Rare Earths, % | 2.0 to 3.0 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.2 |
| Zirconium (Zr), % | 0.4 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.010 | |
| 0 to 0.15 |