EN-MC65210 Magnesium vs. EN 1.0236 Steel

EN-MC65210 magnesium belongs to the magnesium alloys classification, while EN 1.0236 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC65210 magnesium and the bottom bar is EN 1.0236 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 80
140
Elastic (Young's, Tensile) Modulus, GPa 44
190
Elongation at Break, % 2.8
23
Fatigue Strength, MPa 110
230
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
73
Shear Strength, MPa 150
310
Tensile Strength: Ultimate (UTS), MPa 270
490
Tensile Strength: Yield (Proof), MPa 200
330

Thermal Properties

Latent Heat of Fusion, J/g 340
250
Maximum Temperature: Mechanical, °C 170
400
Melting Completion (Liquidus), °C 610
1460
Melting Onset (Solidus), °C 540
1420
Specific Heat Capacity, J/kg-K 970
470
Thermal Conductivity, W/m-K 110
52
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 110
8.2

Otherwise Unclassified Properties

Density, g/cm3 2.0
7.9
Embodied Carbon, kg CO2/kg material 27
1.4
Embodied Energy, MJ/kg 220
18

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.9
99
Resilience: Unit (Modulus of Resilience), kJ/m3 450
290
Stiffness to Weight: Axial, points 12
13
Stiffness to Weight: Bending, points 59
24
Strength to Weight: Axial, points 38
17
Strength to Weight: Bending, points 47
18
Thermal Diffusivity, mm2/s 58
14
Thermal Shock Resistance, points 17
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.21
Copper (Cu), % 0 to 0.030
0
Iron (Fe), % 0 to 0.010
97.9 to 100
Magnesium (Mg), % 92.6 to 95.6
0
Manganese (Mn), % 0 to 0.15
0 to 1.5
Nickel (Ni), % 0 to 0.0050
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.010
0 to 0.3
Silver (Ag), % 2.0 to 3.0
0
Sulfur (S), % 0
0 to 0.035
Unspecified Rare Earths, % 2.0 to 3.0
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0