EN-MC65210 Magnesium vs. EN 1.4113 Stainless Steel

EN-MC65210 magnesium belongs to the magnesium alloys classification, while EN 1.4113 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC65210 magnesium and the bottom bar is EN 1.4113 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 80
180
Elastic (Young's, Tensile) Modulus, GPa 44
200
Elongation at Break, % 2.8
20
Fatigue Strength, MPa 110
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
78
Shear Strength, MPa 150
340
Tensile Strength: Ultimate (UTS), MPa 270
540
Tensile Strength: Yield (Proof), MPa 200
310

Thermal Properties

Latent Heat of Fusion, J/g 340
280
Maximum Temperature: Mechanical, °C 170
880
Melting Completion (Liquidus), °C 610
1450
Melting Onset (Solidus), °C 540
1400
Specific Heat Capacity, J/kg-K 970
480
Thermal Conductivity, W/m-K 110
25
Thermal Expansion, µm/m-K 26
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 110
2.9

Otherwise Unclassified Properties

Density, g/cm3 2.0
7.7
Embodied Carbon, kg CO2/kg material 27
2.4
Embodied Energy, MJ/kg 220
33

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.9
94
Resilience: Unit (Modulus of Resilience), kJ/m3 450
240
Stiffness to Weight: Axial, points 12
14
Stiffness to Weight: Bending, points 59
25
Strength to Weight: Axial, points 38
19
Strength to Weight: Bending, points 47
19
Thermal Diffusivity, mm2/s 58
6.7
Thermal Shock Resistance, points 17
20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.080
Chromium (Cr), % 0
16 to 18
Copper (Cu), % 0 to 0.030
0
Iron (Fe), % 0 to 0.010
78.5 to 83.1
Magnesium (Mg), % 92.6 to 95.6
0
Manganese (Mn), % 0 to 0.15
0 to 1.0
Molybdenum (Mo), % 0
0.9 to 1.4
Nickel (Ni), % 0 to 0.0050
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.010
0 to 1.0
Silver (Ag), % 2.0 to 3.0
0
Sulfur (S), % 0
0 to 0.015
Unspecified Rare Earths, % 2.0 to 3.0
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0