EN-MC65210 Magnesium vs. EN 1.4443 Stainless Steel

EN-MC65210 magnesium belongs to the magnesium alloys classification, while EN 1.4443 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC65210 magnesium and the bottom bar is EN 1.4443 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 80
140
Elastic (Young's, Tensile) Modulus, GPa 44
200
Elongation at Break, % 2.8
34
Fatigue Strength, MPa 110
170
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
78
Tensile Strength: Ultimate (UTS), MPa 270
490
Tensile Strength: Yield (Proof), MPa 200
210

Thermal Properties

Latent Heat of Fusion, J/g 340
300
Maximum Temperature: Mechanical, °C 170
1000
Melting Completion (Liquidus), °C 610
1440
Melting Onset (Solidus), °C 540
1400
Specific Heat Capacity, J/kg-K 970
470
Thermal Conductivity, W/m-K 110
15
Thermal Expansion, µm/m-K 26
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 110
2.4

Otherwise Unclassified Properties

Density, g/cm3 2.0
7.9
Embodied Carbon, kg CO2/kg material 27
4.0
Embodied Energy, MJ/kg 220
54

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.9
140
Resilience: Unit (Modulus of Resilience), kJ/m3 450
110
Stiffness to Weight: Axial, points 12
14
Stiffness to Weight: Bending, points 59
25
Strength to Weight: Axial, points 38
17
Strength to Weight: Bending, points 47
18
Thermal Diffusivity, mm2/s 58
3.9
Thermal Shock Resistance, points 17
11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
18 to 20
Copper (Cu), % 0 to 0.030
0
Iron (Fe), % 0 to 0.010
60.4 to 69.5
Magnesium (Mg), % 92.6 to 95.6
0
Manganese (Mn), % 0 to 0.15
0 to 2.0
Molybdenum (Mo), % 0
2.5 to 3.0
Nickel (Ni), % 0 to 0.0050
10 to 13
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.010
0 to 1.5
Silver (Ag), % 2.0 to 3.0
0
Sulfur (S), % 0
0 to 0.030
Unspecified Rare Earths, % 2.0 to 3.0
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0