EN-MC65210 Magnesium vs. C14300 Copper

EN-MC65210 magnesium belongs to the magnesium alloys classification, while C14300 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC65210 magnesium and the bottom bar is C14300 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
120
Elongation at Break, % 2.8
2.0 to 42
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 17
43
Shear Strength, MPa 150
150 to 260
Tensile Strength: Ultimate (UTS), MPa 270
220 to 460
Tensile Strength: Yield (Proof), MPa 200
76 to 430

Thermal Properties

Latent Heat of Fusion, J/g 340
210
Maximum Temperature: Mechanical, °C 170
220
Melting Completion (Liquidus), °C 610
1080
Melting Onset (Solidus), °C 540
1050
Specific Heat Capacity, J/kg-K 970
390
Thermal Conductivity, W/m-K 110
380
Thermal Expansion, µm/m-K 26
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
96
Electrical Conductivity: Equal Weight (Specific), % IACS 110
96

Otherwise Unclassified Properties

Density, g/cm3 2.0
9.0
Embodied Carbon, kg CO2/kg material 27
2.6
Embodied Energy, MJ/kg 220
41

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.9
9.0 to 72
Resilience: Unit (Modulus of Resilience), kJ/m3 450
25 to 810
Stiffness to Weight: Axial, points 12
7.2
Stiffness to Weight: Bending, points 59
18
Strength to Weight: Axial, points 38
6.8 to 14
Strength to Weight: Bending, points 47
9.1 to 15
Thermal Diffusivity, mm2/s 58
110
Thermal Shock Resistance, points 17
7.8 to 16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Cadmium (Cd), % 0
0.050 to 0.15
Copper (Cu), % 0 to 0.030
99.9 to 99.95
Iron (Fe), % 0 to 0.010
0
Magnesium (Mg), % 92.6 to 95.6
0
Manganese (Mn), % 0 to 0.15
0
Nickel (Ni), % 0 to 0.0050
0
Silicon (Si), % 0 to 0.010
0
Silver (Ag), % 2.0 to 3.0
0
Unspecified Rare Earths, % 2.0 to 3.0
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0