EN-MC65220 Magnesium vs. 8090 Aluminum
EN-MC65220 magnesium belongs to the magnesium alloys classification, while 8090 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN-MC65220 magnesium and the bottom bar is 8090 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 67 |
| Elongation at Break, % | 2.2 | |
| 3.5 to 13 |
| Fatigue Strength, MPa | 110 | |
| 91 to 140 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 17 | |
| 25 |
| Tensile Strength: Ultimate (UTS), MPa | 270 | |
| 340 to 490 |
| Tensile Strength: Yield (Proof), MPa | 200 | |
| 210 to 420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 190 |
| Melting Completion (Liquidus), °C | 610 | |
| 660 |
| Melting Onset (Solidus), °C | 550 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 980 | |
| 960 |
| Thermal Conductivity, W/m-K | 110 | |
| 95 to 160 |
| Thermal Expansion, µm/m-K | 26 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 20 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 66 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 80 | |
| 18 |
| Density, g/cm3 | 1.9 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 27 | |
| 8.6 |
| Embodied Energy, MJ/kg | 210 | |
| 170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 5.5 | |
| 16 to 41 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 450 | |
| 340 to 1330 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 62 | |
| 50 |
| Strength to Weight: Axial, points | 40 | |
| 34 to 49 |
| Strength to Weight: Bending, points | 49 | |
| 39 to 50 |
| Thermal Diffusivity, mm2/s | 61 | |
| 36 to 60 |
| Thermal Shock Resistance, points | 17 | |
| 15 to 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 93 to 98.4 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0.050 to 0.1 | |
| 1.0 to 1.6 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.3 |
| Lithium (Li), % | 0 | |
| 2.2 to 2.7 |
| Magnesium (Mg), % | 93.8 to 96.8 | |
| 0.6 to 1.3 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 0.2 |
| Silver (Ag), % | 1.3 to 1.7 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Unspecified Rare Earths, % | 1.5 to 3.0 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.25 |
| Zirconium (Zr), % | 0.4 to 1.0 | |
| 0.040 to 0.16 |
| Residuals, % | 0 to 0.010 | |
| 0 to 0.15 |