Menu (ESC)

EN-MC65220 Magnesium vs. AWS ENiCrMo-10

EN-MC65220 magnesium belongs to the magnesium alloys classification, while AWS ENiCrMo-10 belongs to the nickel alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC65220 magnesium and the bottom bar is AWS ENiCrMo-10.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
220
Elongation at Break, % 2.2
28
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
84
Tensile Strength: Ultimate (UTS), MPa 270
710

Thermal Properties

Latent Heat of Fusion, J/g 340
320
Melting Completion (Liquidus), °C 610
1550
Melting Onset (Solidus), °C 550
1490
Specific Heat Capacity, J/kg-K 980
420
Thermal Conductivity, W/m-K 110
10
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 120
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 80
70
Density, g/cm3 1.9
8.9
Embodied Carbon, kg CO2/kg material 27
12
Embodied Energy, MJ/kg 210
160

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 62
23
Strength to Weight: Axial, points 40
22
Strength to Weight: Bending, points 49
20
Thermal Diffusivity, mm2/s 61
2.7
Thermal Shock Resistance, points 17
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0
20 to 22.5
Cobalt (Co), % 0
0 to 2.5
Copper (Cu), % 0.050 to 0.1
0 to 0.5
Iron (Fe), % 0 to 0.010
2.0 to 6.0
Magnesium (Mg), % 93.8 to 96.8
0
Manganese (Mn), % 0 to 0.15
0 to 1.0
Molybdenum (Mo), % 0
12.5 to 14.5
Nickel (Ni), % 0 to 0.0050
48.4 to 63
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.010
0 to 0.2
Silver (Ag), % 1.3 to 1.7
0
Sulfur (S), % 0
0 to 0.015
Tungsten (W), % 0
2.5 to 3.5
Unspecified Rare Earths, % 1.5 to 3.0
0
Vanadium (V), % 0
0 to 0.35
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0 to 0.5