EN-MC65220 Magnesium vs. EN 1.0601 Steel

EN-MC65220 magnesium belongs to the magnesium alloys classification, while EN 1.0601 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC65220 magnesium and the bottom bar is EN 1.0601 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 80
210
Elastic (Young's, Tensile) Modulus, GPa 44
190
Elongation at Break, % 2.2
11
Fatigue Strength, MPa 110
220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
72
Shear Strength, MPa 150
430
Tensile Strength: Ultimate (UTS), MPa 270
730
Tensile Strength: Yield (Proof), MPa 200
350

Thermal Properties

Latent Heat of Fusion, J/g 340
250
Maximum Temperature: Mechanical, °C 160
400
Melting Completion (Liquidus), °C 610
1460
Melting Onset (Solidus), °C 550
1410
Specific Heat Capacity, J/kg-K 980
470
Thermal Conductivity, W/m-K 110
48
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 120
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 80
2.1
Density, g/cm3 1.9
7.8
Embodied Carbon, kg CO2/kg material 27
1.5
Embodied Energy, MJ/kg 210
19

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.5
65
Resilience: Unit (Modulus of Resilience), kJ/m3 450
330
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 62
24
Strength to Weight: Axial, points 40
26
Strength to Weight: Bending, points 49
23
Thermal Diffusivity, mm2/s 61
13
Thermal Shock Resistance, points 17
23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.57 to 0.65
Chromium (Cr), % 0
0 to 0.4
Copper (Cu), % 0.050 to 0.1
0
Iron (Fe), % 0 to 0.010
97.1 to 98.8
Magnesium (Mg), % 93.8 to 96.8
0
Manganese (Mn), % 0 to 0.15
0.6 to 0.9
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 0 to 0.0050
0 to 0.4
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.010
0 to 0.4
Silver (Ag), % 1.3 to 1.7
0
Sulfur (S), % 0
0 to 0.045
Unspecified Rare Earths, % 1.5 to 3.0
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0