EN-MC65220 Magnesium vs. EN 1.4405 Stainless Steel

EN-MC65220 magnesium belongs to the magnesium alloys classification, while EN 1.4405 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC65220 magnesium and the bottom bar is EN 1.4405 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
200
Elongation at Break, % 2.2
17
Fatigue Strength, MPa 110
370
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
77
Tensile Strength: Ultimate (UTS), MPa 270
860
Tensile Strength: Yield (Proof), MPa 200
610

Thermal Properties

Latent Heat of Fusion, J/g 340
280
Maximum Temperature: Mechanical, °C 160
870
Melting Completion (Liquidus), °C 610
1450
Melting Onset (Solidus), °C 550
1400
Specific Heat Capacity, J/kg-K 980
480
Thermal Conductivity, W/m-K 110
17
Thermal Expansion, µm/m-K 26
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 120
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 80
13
Density, g/cm3 1.9
7.8
Embodied Carbon, kg CO2/kg material 27
2.8
Embodied Energy, MJ/kg 210
39

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.5
130
Resilience: Unit (Modulus of Resilience), kJ/m3 450
950
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 62
25
Strength to Weight: Axial, points 40
31
Strength to Weight: Bending, points 49
26
Thermal Diffusivity, mm2/s 61
4.6
Thermal Shock Resistance, points 17
29

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.060
Chromium (Cr), % 0
15 to 17
Copper (Cu), % 0.050 to 0.1
0
Iron (Fe), % 0 to 0.010
73.6 to 80.3
Magnesium (Mg), % 93.8 to 96.8
0
Manganese (Mn), % 0 to 0.15
0 to 1.0
Molybdenum (Mo), % 0
0.7 to 1.5
Nickel (Ni), % 0 to 0.0050
4.0 to 6.0
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 0.010
0 to 0.8
Silver (Ag), % 1.3 to 1.7
0
Sulfur (S), % 0
0 to 0.025
Unspecified Rare Earths, % 1.5 to 3.0
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0