EN-MC65220 Magnesium vs. EN AC-44300 Aluminum

EN-MC65220 magnesium belongs to the magnesium alloys classification, while EN AC-44300 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN-MC65220 magnesium and the bottom bar is EN AC-44300 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 80
68
Elastic (Young's, Tensile) Modulus, GPa 44
72
Elongation at Break, % 2.2
1.1
Fatigue Strength, MPa 110
100
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 17
27
Tensile Strength: Ultimate (UTS), MPa 270
270
Tensile Strength: Yield (Proof), MPa 200
150

Thermal Properties

Latent Heat of Fusion, J/g 340
570
Maximum Temperature: Mechanical, °C 160
170
Melting Completion (Liquidus), °C 610
590
Melting Onset (Solidus), °C 550
580
Specific Heat Capacity, J/kg-K 980
900
Thermal Conductivity, W/m-K 110
130
Thermal Expansion, µm/m-K 26
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
33
Electrical Conductivity: Equal Weight (Specific), % IACS 120
120

Otherwise Unclassified Properties

Base Metal Price, % relative 80
9.5
Density, g/cm3 1.9
2.5
Embodied Carbon, kg CO2/kg material 27
7.7
Embodied Energy, MJ/kg 210
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.5
2.6
Resilience: Unit (Modulus of Resilience), kJ/m3 450
150
Stiffness to Weight: Axial, points 13
16
Stiffness to Weight: Bending, points 62
55
Strength to Weight: Axial, points 40
29
Strength to Weight: Bending, points 49
36
Thermal Diffusivity, mm2/s 61
58
Thermal Shock Resistance, points 17
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
84.3 to 89.5
Copper (Cu), % 0.050 to 0.1
0 to 0.1
Iron (Fe), % 0 to 0.010
0 to 1.0
Magnesium (Mg), % 93.8 to 96.8
0
Manganese (Mn), % 0 to 0.15
0 to 0.55
Nickel (Ni), % 0 to 0.0050
0
Silicon (Si), % 0 to 0.010
10.5 to 13.5
Silver (Ag), % 1.3 to 1.7
0
Titanium (Ti), % 0
0 to 0.15
Unspecified Rare Earths, % 1.5 to 3.0
0
Zinc (Zn), % 0 to 0.2
0 to 0.15
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0 to 0.25