EN-MC65220 Magnesium vs. SAE-AISI F1 Steel

EN-MC65220 magnesium belongs to the magnesium alloys classification, while SAE-AISI F1 steel belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC65220 magnesium and the bottom bar is SAE-AISI F1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
72
Tensile Strength: Ultimate (UTS), MPa 270
620 to 2320

Thermal Properties

Latent Heat of Fusion, J/g 340
250
Melting Completion (Liquidus), °C 610
1480
Melting Onset (Solidus), °C 550
1430
Specific Heat Capacity, J/kg-K 980
470
Thermal Conductivity, W/m-K 110
45
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 120
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 80
5.0
Density, g/cm3 1.9
7.9
Embodied Carbon, kg CO2/kg material 27
1.7
Embodied Energy, MJ/kg 210
24

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 62
24
Strength to Weight: Axial, points 40
22 to 82
Strength to Weight: Bending, points 49
20 to 49
Thermal Diffusivity, mm2/s 61
12
Thermal Shock Resistance, points 17
19 to 70

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
1.0 to 1.3
Copper (Cu), % 0.050 to 0.1
0
Iron (Fe), % 0 to 0.010
95.9 to 98
Magnesium (Mg), % 93.8 to 96.8
0
Manganese (Mn), % 0 to 0.15
0 to 0.5
Nickel (Ni), % 0 to 0.0050
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.010
0.1 to 0.5
Silver (Ag), % 1.3 to 1.7
0
Sulfur (S), % 0
0 to 0.030
Tungsten (W), % 0
1.0 to 1.8
Unspecified Rare Earths, % 1.5 to 3.0
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0