EN-MC65220 Magnesium vs. C12200 Copper

EN-MC65220 magnesium belongs to the magnesium alloys classification, while C12200 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC65220 magnesium and the bottom bar is C12200 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
120
Elongation at Break, % 2.2
3.2 to 50
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 17
43
Shear Strength, MPa 150
150 to 240
Tensile Strength: Ultimate (UTS), MPa 270
220 to 410
Tensile Strength: Yield (Proof), MPa 200
69 to 400

Thermal Properties

Latent Heat of Fusion, J/g 340
210
Maximum Temperature: Mechanical, °C 160
200
Melting Completion (Liquidus), °C 610
1080
Melting Onset (Solidus), °C 550
1030
Specific Heat Capacity, J/kg-K 980
390
Thermal Conductivity, W/m-K 110
340
Thermal Expansion, µm/m-K 26
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
85
Electrical Conductivity: Equal Weight (Specific), % IACS 120
85

Otherwise Unclassified Properties

Base Metal Price, % relative 80
31
Density, g/cm3 1.9
9.0
Embodied Carbon, kg CO2/kg material 27
2.6
Embodied Energy, MJ/kg 210
41

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.5
11 to 91
Resilience: Unit (Modulus of Resilience), kJ/m3 450
21 to 690
Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 62
18
Strength to Weight: Axial, points 40
6.9 to 13
Strength to Weight: Bending, points 49
9.1 to 14
Thermal Diffusivity, mm2/s 61
98
Thermal Shock Resistance, points 17
7.9 to 15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 0.050 to 0.1
99.9 to 99.985
Iron (Fe), % 0 to 0.010
0
Magnesium (Mg), % 93.8 to 96.8
0
Manganese (Mn), % 0 to 0.15
0
Nickel (Ni), % 0 to 0.0050
0
Phosphorus (P), % 0
0.015 to 0.040
Silicon (Si), % 0 to 0.010
0
Silver (Ag), % 1.3 to 1.7
0
Unspecified Rare Earths, % 1.5 to 3.0
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0