EN-MC65220 Magnesium vs. S82013 Stainless Steel

EN-MC65220 magnesium belongs to the magnesium alloys classification, while S82013 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC65220 magnesium and the bottom bar is S82013 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 80
260
Elastic (Young's, Tensile) Modulus, GPa 44
200
Elongation at Break, % 2.2
34
Fatigue Strength, MPa 110
400
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
78
Shear Strength, MPa 150
470
Tensile Strength: Ultimate (UTS), MPa 270
710
Tensile Strength: Yield (Proof), MPa 200
500

Thermal Properties

Latent Heat of Fusion, J/g 340
290
Maximum Temperature: Mechanical, °C 160
970
Melting Completion (Liquidus), °C 610
1420
Melting Onset (Solidus), °C 550
1380
Specific Heat Capacity, J/kg-K 980
480
Thermal Conductivity, W/m-K 110
15
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 120
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 80
11
Density, g/cm3 1.9
7.7
Embodied Carbon, kg CO2/kg material 27
2.4
Embodied Energy, MJ/kg 210
34

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.5
220
Resilience: Unit (Modulus of Resilience), kJ/m3 450
640
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 62
25
Strength to Weight: Axial, points 40
26
Strength to Weight: Bending, points 49
23
Thermal Diffusivity, mm2/s 61
4.0
Thermal Shock Resistance, points 17
20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.060
Chromium (Cr), % 0
19.5 to 22
Copper (Cu), % 0.050 to 0.1
0.2 to 1.2
Iron (Fe), % 0 to 0.010
70.5 to 77.1
Magnesium (Mg), % 93.8 to 96.8
0
Manganese (Mn), % 0 to 0.15
2.5 to 3.5
Nickel (Ni), % 0 to 0.0050
0.5 to 1.5
Nitrogen (N), % 0
0.2 to 0.3
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.010
0 to 0.9
Silver (Ag), % 1.3 to 1.7
0
Sulfur (S), % 0
0 to 0.030
Unspecified Rare Earths, % 1.5 to 3.0
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0