EN-MC95310 Magnesium vs. 4015 Aluminum
EN-MC95310 magnesium belongs to the magnesium alloys classification, while 4015 aluminum belongs to the aluminum alloys.
For each property being compared, the top bar is EN-MC95310 magnesium and the bottom bar is 4015 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 85 | |
| 35 to 70 |
| Elastic (Young's, Tensile) Modulus, GPa | 45 | |
| 70 |
| Elongation at Break, % | 2.2 | |
| 1.1 to 23 |
| Fatigue Strength, MPa | 110 | |
| 46 to 71 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 17 | |
| 26 |
| Shear Strength, MPa | 160 | |
| 82 to 120 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 130 to 220 |
| Tensile Strength: Yield (Proof), MPa | 190 | |
| 50 to 200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 160 |
| Melting Completion (Liquidus), °C | 650 | |
| 640 |
| Melting Onset (Solidus), °C | 540 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 960 | |
| 900 |
| Thermal Conductivity, W/m-K | 51 | |
| 160 |
| Thermal Expansion, µm/m-K | 25 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 41 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 50 | |
| 130 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 34 | |
| 9.5 |
| Density, g/cm3 | 1.9 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 29 | |
| 8.1 |
| Embodied Energy, MJ/kg | 260 | |
| 150 |
| Embodied Water, L/kg | 900 | |
| 1160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 5.6 | |
| 2.4 to 24 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 420 | |
| 18 to 290 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 61 | |
| 50 |
| Strength to Weight: Axial, points | 40 | |
| 13 to 22 |
| Strength to Weight: Bending, points | 49 | |
| 21 to 30 |
| Thermal Diffusivity, mm2/s | 28 | |
| 66 |
| Thermal Shock Resistance, points | 18 | |
| 5.7 to 9.7 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 94.9 to 97.9 |
| Copper (Cu), % | 0 to 0.030 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.7 |
| Lithium (Li), % | 0 to 0.2 | |
| 0 |
| Magnesium (Mg), % | 88.9 to 93.4 | |
| 0.1 to 0.5 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0.6 to 1.2 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 |
| Silicon (Si), % | 0 to 0.010 | |
| 1.4 to 2.2 |
| Unspecified Rare Earths, % | 1.5 to 4.0 | |
| 0 |
| Yttrium (Y), % | 4.8 to 5.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.2 |
| Zirconium (Zr), % | 0.4 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.010 | |
| 0 to 0.15 |