EN-MC95310 Magnesium vs. AISI 440C Stainless Steel

EN-MC95310 magnesium belongs to the magnesium alloys classification, while AISI 440C stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC95310 magnesium and the bottom bar is AISI 440C stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
200
Elongation at Break, % 2.2
2.0 to 14
Fatigue Strength, MPa 110
260 to 840
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
76
Shear Strength, MPa 160
430 to 1120
Tensile Strength: Ultimate (UTS), MPa 280
710 to 1970
Tensile Strength: Yield (Proof), MPa 190
450 to 1900

Thermal Properties

Latent Heat of Fusion, J/g 330
280
Maximum Temperature: Mechanical, °C 170
870
Melting Completion (Liquidus), °C 650
1480
Melting Onset (Solidus), °C 540
1370
Specific Heat Capacity, J/kg-K 960
480
Thermal Conductivity, W/m-K 51
22
Thermal Expansion, µm/m-K 25
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 50
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 34
9.0
Density, g/cm3 1.9
7.7
Embodied Carbon, kg CO2/kg material 29
2.2
Embodied Energy, MJ/kg 260
31
Embodied Water, L/kg 900
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.6
39 to 88
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 61
25
Strength to Weight: Axial, points 40
26 to 71
Strength to Weight: Bending, points 49
23 to 46
Thermal Diffusivity, mm2/s 28
6.0
Thermal Shock Resistance, points 18
26 to 71

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
1.0 to 1.2
Chromium (Cr), % 0
16 to 18
Copper (Cu), % 0 to 0.030
0
Iron (Fe), % 0 to 0.010
78 to 83.1
Lithium (Li), % 0 to 0.2
0
Magnesium (Mg), % 88.9 to 93.4
0
Manganese (Mn), % 0 to 0.15
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 0 to 0.0050
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.010
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Unspecified Rare Earths, % 1.5 to 4.0
0
Yttrium (Y), % 4.8 to 5.5
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0