EN-MC95310 Magnesium vs. AWS E349

EN-MC95310 magnesium belongs to the magnesium alloys classification, while AWS E349 belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC95310 magnesium and the bottom bar is AWS E349.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
200
Elongation at Break, % 2.2
29
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
78
Tensile Strength: Ultimate (UTS), MPa 280
770

Thermal Properties

Latent Heat of Fusion, J/g 330
290
Melting Completion (Liquidus), °C 650
1470
Melting Onset (Solidus), °C 540
1420
Specific Heat Capacity, J/kg-K 960
470
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 25
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 50
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 34
25
Density, g/cm3 1.9
7.9
Embodied Carbon, kg CO2/kg material 29
4.9
Embodied Energy, MJ/kg 260
72
Embodied Water, L/kg 900
150

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 61
25
Strength to Weight: Axial, points 40
27
Strength to Weight: Bending, points 49
24
Thermal Diffusivity, mm2/s 28
4.1
Thermal Shock Resistance, points 18
20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.13
Chromium (Cr), % 0
18 to 21
Copper (Cu), % 0 to 0.030
0 to 0.75
Iron (Fe), % 0 to 0.010
60.5 to 71.1
Lithium (Li), % 0 to 0.2
0
Magnesium (Mg), % 88.9 to 93.4
0
Manganese (Mn), % 0 to 0.15
0.5 to 2.5
Molybdenum (Mo), % 0
0.35 to 0.65
Nickel (Ni), % 0 to 0.0050
8.0 to 10
Niobium (Nb), % 0
0.75 to 1.2
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.010
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0
0 to 0.15
Tungsten (W), % 0
1.3 to 1.8
Unspecified Rare Earths, % 1.5 to 4.0
0
Vanadium (V), % 0
0.1 to 0.3
Yttrium (Y), % 4.8 to 5.5
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010