EN-MC95310 Magnesium vs. EN 1.3961 Alloy

EN-MC95310 magnesium belongs to the magnesium alloys classification, while EN 1.3961 alloy belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC95310 magnesium and the bottom bar is EN 1.3961 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
190
Elongation at Break, % 2.2
31
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 17
72
Shear Strength, MPa 160
300
Tensile Strength: Ultimate (UTS), MPa 280
450
Tensile Strength: Yield (Proof), MPa 190
310

Thermal Properties

Latent Heat of Fusion, J/g 330
270
Melting Completion (Liquidus), °C 650
1430
Melting Onset (Solidus), °C 540
1390
Specific Heat Capacity, J/kg-K 960
460
Thermal Expansion, µm/m-K 25
1.3

Otherwise Unclassified Properties

Base Metal Price, % relative 34
25
Density, g/cm3 1.9
8.2
Embodied Carbon, kg CO2/kg material 29
4.8
Embodied Energy, MJ/kg 260
66
Embodied Water, L/kg 900
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.6
130
Resilience: Unit (Modulus of Resilience), kJ/m3 420
250
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 61
23
Strength to Weight: Axial, points 40
15
Strength to Weight: Bending, points 49
16
Thermal Shock Resistance, points 18
130

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
0 to 0.25
Copper (Cu), % 0 to 0.030
0
Iron (Fe), % 0 to 0.010
60.7 to 65
Lithium (Li), % 0 to 0.2
0
Magnesium (Mg), % 88.9 to 93.4
0
Manganese (Mn), % 0 to 0.15
0 to 0.5
Molybdenum (Mo), % 0
0 to 1.0
Nickel (Ni), % 0 to 0.0050
35 to 37
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.010
0 to 0.5
Sulfur (S), % 0
0 to 0.020
Unspecified Rare Earths, % 1.5 to 4.0
0
Yttrium (Y), % 4.8 to 5.5
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0