EN-MC95310 Magnesium vs. EN 1.4372 Stainless Steel

EN-MC95310 magnesium belongs to the magnesium alloys classification, while EN 1.4372 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC95310 magnesium and the bottom bar is EN 1.4372 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 85
220
Elastic (Young's, Tensile) Modulus, GPa 45
200
Elongation at Break, % 2.2
47
Fatigue Strength, MPa 110
330
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
77
Shear Strength, MPa 160
560
Tensile Strength: Ultimate (UTS), MPa 280
790
Tensile Strength: Yield (Proof), MPa 190
350

Thermal Properties

Latent Heat of Fusion, J/g 330
280
Maximum Temperature: Mechanical, °C 170
880
Melting Completion (Liquidus), °C 650
1410
Melting Onset (Solidus), °C 540
1370
Specific Heat Capacity, J/kg-K 960
480
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 25
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 50
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 34
12
Density, g/cm3 1.9
7.7
Embodied Carbon, kg CO2/kg material 29
2.6
Embodied Energy, MJ/kg 260
38
Embodied Water, L/kg 900
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.6
310
Resilience: Unit (Modulus of Resilience), kJ/m3 420
320
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 61
25
Strength to Weight: Axial, points 40
29
Strength to Weight: Bending, points 49
25
Thermal Diffusivity, mm2/s 28
4.0
Thermal Shock Resistance, points 18
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.15
Chromium (Cr), % 0
16 to 18
Copper (Cu), % 0 to 0.030
0
Iron (Fe), % 0 to 0.010
67.5 to 75
Lithium (Li), % 0 to 0.2
0
Magnesium (Mg), % 88.9 to 93.4
0
Manganese (Mn), % 0 to 0.15
5.5 to 7.5
Nickel (Ni), % 0 to 0.0050
3.5 to 5.5
Nitrogen (N), % 0
0.050 to 0.25
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.010
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Unspecified Rare Earths, % 1.5 to 4.0
0
Yttrium (Y), % 4.8 to 5.5
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0