EN-MC95310 Magnesium vs. Grade 365 Molybdenum

EN-MC95310 magnesium belongs to the magnesium alloys classification, while grade 365 molybdenum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC95310 magnesium and the bottom bar is grade 365 molybdenum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
310
Elongation at Break, % 2.2
6.3
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 17
120
Tensile Strength: Ultimate (UTS), MPa 280
620
Tensile Strength: Yield (Proof), MPa 190
530

Thermal Properties

Latent Heat of Fusion, J/g 330
370
Specific Heat Capacity, J/kg-K 960
250
Thermal Expansion, µm/m-K 25
7.0

Otherwise Unclassified Properties

Density, g/cm3 1.9
10
Embodied Carbon, kg CO2/kg material 29
28
Embodied Energy, MJ/kg 260
330
Embodied Water, L/kg 900
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.6
37
Resilience: Unit (Modulus of Resilience), kJ/m3 420
450
Stiffness to Weight: Axial, points 13
17
Stiffness to Weight: Bending, points 61
22
Strength to Weight: Axial, points 40
17
Strength to Weight: Bending, points 49
16
Thermal Shock Resistance, points 18
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.010
Copper (Cu), % 0 to 0.030
0
Iron (Fe), % 0 to 0.010
0 to 0.010
Lithium (Li), % 0 to 0.2
0
Magnesium (Mg), % 88.9 to 93.4
0
Manganese (Mn), % 0 to 0.15
0
Molybdenum (Mo), % 0
99.9 to 100
Nickel (Ni), % 0 to 0.0050
0 to 0.0020
Nitrogen (N), % 0
0 to 0.0020
Oxygen (O), % 0
0 to 0.0015
Silicon (Si), % 0 to 0.010
0 to 0.010
Unspecified Rare Earths, % 1.5 to 4.0
0
Yttrium (Y), % 4.8 to 5.5
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0