EN-MC95310 Magnesium vs. SAE-AISI 1046 Steel

EN-MC95310 magnesium belongs to the magnesium alloys classification, while SAE-AISI 1046 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC95310 magnesium and the bottom bar is SAE-AISI 1046 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 85
190 to 210
Elastic (Young's, Tensile) Modulus, GPa 45
190
Elongation at Break, % 2.2
14 to 17
Fatigue Strength, MPa 110
240 to 390
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
72
Shear Strength, MPa 160
410 to 450
Tensile Strength: Ultimate (UTS), MPa 280
660 to 740
Tensile Strength: Yield (Proof), MPa 190
370 to 610

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 170
400
Melting Completion (Liquidus), °C 650
1460
Melting Onset (Solidus), °C 540
1420
Specific Heat Capacity, J/kg-K 960
470
Thermal Conductivity, W/m-K 51
51
Thermal Expansion, µm/m-K 25
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
11
Electrical Conductivity: Equal Weight (Specific), % IACS 50
12

Otherwise Unclassified Properties

Base Metal Price, % relative 34
1.8
Density, g/cm3 1.9
7.8
Embodied Carbon, kg CO2/kg material 29
1.4
Embodied Energy, MJ/kg 260
18
Embodied Water, L/kg 900
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.6
91 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 420
360 to 990
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 61
24
Strength to Weight: Axial, points 40
23 to 26
Strength to Weight: Bending, points 49
22 to 23
Thermal Diffusivity, mm2/s 28
14
Thermal Shock Resistance, points 18
23 to 25

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.43 to 0.5
Copper (Cu), % 0 to 0.030
0
Iron (Fe), % 0 to 0.010
98.4 to 98.9
Lithium (Li), % 0 to 0.2
0
Magnesium (Mg), % 88.9 to 93.4
0
Manganese (Mn), % 0 to 0.15
0.7 to 1.0
Nickel (Ni), % 0 to 0.0050
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.010
0
Sulfur (S), % 0
0 to 0.050
Unspecified Rare Earths, % 1.5 to 4.0
0
Yttrium (Y), % 4.8 to 5.5
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0