EN-MC95310 Magnesium vs. C92300 Bronze

EN-MC95310 magnesium belongs to the magnesium alloys classification, while C92300 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC95310 magnesium and the bottom bar is C92300 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
110
Elongation at Break, % 2.2
19
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 17
40
Tensile Strength: Ultimate (UTS), MPa 280
300
Tensile Strength: Yield (Proof), MPa 190
140

Thermal Properties

Latent Heat of Fusion, J/g 330
190
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 650
1000
Melting Onset (Solidus), °C 540
850
Specific Heat Capacity, J/kg-K 960
370
Thermal Conductivity, W/m-K 51
75
Thermal Expansion, µm/m-K 25
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
12
Electrical Conductivity: Equal Weight (Specific), % IACS 50
12

Otherwise Unclassified Properties

Base Metal Price, % relative 34
33
Density, g/cm3 1.9
8.7
Embodied Carbon, kg CO2/kg material 29
3.4
Embodied Energy, MJ/kg 260
56
Embodied Water, L/kg 900
370

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.6
47
Resilience: Unit (Modulus of Resilience), kJ/m3 420
86
Stiffness to Weight: Axial, points 13
6.9
Stiffness to Weight: Bending, points 61
18
Strength to Weight: Axial, points 40
9.5
Strength to Weight: Bending, points 49
11
Thermal Diffusivity, mm2/s 28
23
Thermal Shock Resistance, points 18
11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Copper (Cu), % 0 to 0.030
85 to 89
Iron (Fe), % 0 to 0.010
0 to 0.25
Lead (Pb), % 0
0.3 to 1.0
Lithium (Li), % 0 to 0.2
0
Magnesium (Mg), % 88.9 to 93.4
0
Manganese (Mn), % 0 to 0.15
0
Nickel (Ni), % 0 to 0.0050
0 to 1.0
Phosphorus (P), % 0
0 to 1.5
Silicon (Si), % 0 to 0.010
0 to 0.0050
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0
7.5 to 9.0
Unspecified Rare Earths, % 1.5 to 4.0
0
Yttrium (Y), % 4.8 to 5.5
0
Zinc (Zn), % 0 to 0.2
2.5 to 5.0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0 to 0.7