EQ21A magnesium belongs to the magnesium alloys classification, while AWS BVAg-6b belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EQ21A magnesium and the bottom bar is AWS BVAg-6b.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
93
Poisson's Ratio 0.29
0.35
Shear Modulus, GPa 17
35
Tensile Strength: Ultimate (UTS), MPa 250
180

Thermal Properties

Latent Heat of Fusion, J/g 340
160
Melting Completion (Liquidus), °C 640
870
Melting Onset (Solidus), °C 560
780
Specific Heat Capacity, J/kg-K 980
310
Thermal Expansion, µm/m-K 27
19

Otherwise Unclassified Properties

Density, g/cm3 1.9
9.7
Embodied Carbon, kg CO2/kg material 27
49
Embodied Energy, MJ/kg 210
770

Common Calculations

Stiffness to Weight: Axial, points 13
5.3
Stiffness to Weight: Bending, points 63
16
Strength to Weight: Axial, points 37
5.1
Strength to Weight: Bending, points 47
7.3
Thermal Shock Resistance, points 15
7.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0
0 to 0.0050
Copper (Cu), % 0.050 to 0.1
49 to 51
Lead (Pb), % 0
0 to 0.0020
Magnesium (Mg), % 93.9 to 96.8
0
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0
0 to 0.0020
Silver (Ag), % 1.3 to 1.7
49 to 51
Unspecified Rare Earths, % 1.5 to 3.0
0
Zinc (Zn), % 0
0 to 0.0010
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.3
0